Jpn. J. Appl. Phys. 26 (1987) pp. L709-L710 |Next Article| |Table of Contents|
|Full Text PDF (253K)| |Buy This Article|
Letter
Preparation and Characterization of Superconducting Y-Ba-Cu-O Thin Films
Hideaki Adachi,
Kentaro Setsune,
Tsuneo Mitsuyu,
Kumiko Hirochi,
Yo Ichikawa,
Takeshi Kamada and
Kiyotaka Wasa
Central Research Laboratories, Matsushita Electric Industrial Co., Ltd.
(Received April 15, 1987; accepted for publication April 25, 1987)
Thin films of Y-Ba-Cu-O system have been prepared by rf-magnetron sputtering technique. The films were crystallized through post annealing and superconductivity was appeared. The film on R-plane of sapphire showed superconducting transition with an onset temperature at 94 K and zero-ρ state was achieved below 70 K.
URL:
http://jjap.jsap.jp/link?JJAP/26/L709/
DOI: 10.1143/JJAP.26.L709
- J. G. Bednorz and K. A. Muller:
Z. Phys. B 64 (1986) 189[CrossRef].
- S. Uchida, H. Takagi, K. Kitazawa and S. Tanaka:
Jpn. J. Appl. Phys. 26 (1987) L1[JSAP].
- H. Takagi, S. Uchida, K. Kitazawa and S. Tanaka:
Jpn. J. Appl. Phys. 26 (1987) L123[JSAP].
- S. Uchida, H. Takagi, K. Kitazawa and S. Tanaka:
Jpn. J. Appl. Phys. 26 (1987) L151[JSAP].
- C. W. Chu, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang and Y. Q. Wang:
Phys. Rev. Lett. 58 (1987) 405[APS].
- R. J. Cava, R. B. van Dover, B. Batlogg and E. A. Rietman:
Phys. Rev. Lett. 58 (1987) 408[APS].
- D. W. Caponell, D. G. Hinks, J. D. Jorgensen and K. Zhang:
Appl. Phys. Lett. 50 (1987) 543[AIP Scitation].
- M. K. Wu, J. R. Ashburn, C. J. Torng, P. H. Hor, R. L. Meng, L. Gao, Z. J. Huang, Y. Q. Wang and C. W. Chu:
Phys. Rev. Lett. 58 (1987) 908[APS].
- P. H. Hor, L. Gao, R. L. Meng, Z. J. Huang, Y. Q. Wang, K. Forster, J. Vassilious, C. W. Chu, M. K. Wu, J. R. Ashburn and C. J. Torng:
Phys. Rev. Lett. 58 (1987) 911[APS].
- H. Adachi, K. Setsune and K. Wasa: submitted to Phys. Rev. Lett.