Jpn. J. Appl. Phys. 45 (2006) pp. L690-L693 |Previous Article| |Next Article| |Table of Contents|
|Full Text PDF (125K)| |Buy This Article|
Letter
Evaluation of Crystallinity in 4H–SiC{0001} Epilayers Thermally Etched by Chlorine and Oxygen System
Tomoaki Hatayama,
Hiroshi Yano,
Yukiharu Uraoka and
Takashi Fuyuki
Graduate School of Materials Science, Nara Institute of Science and Technology, 8916-5 Takayama, Ikoma, Nara 630-0192, Japan
(Received May 15, 2006; accepted May 25, 2006; published online July 7, 2006)
A thermal etching with a mixed gas of chlorine and oxygen was applied to analyze the crystal defects in 4H–SiC{0001} epilayers for the first time. The etching rate of the (0001)Si face was more one-tenth slower than that of the (000\bar)C face. Etch pits and oval hillocks were observed on the (0001)Si and (0001)C faces, respectively. The shapes of the etch pits were similar to those in the case of etching by a molten potassium-hydroxide method. The etch pits on the (0001)Si face were minority carrier traps as confirmed by a planar mapping electron-beam-induced current method. On the other hand, oval hillocks on the etched (0001)C face were not minority carrier traps. On the basis of these results, etching mechanisms are discussed.
URL:
http://jjap.jsap.jp/link?JJAP/45/L690/
DOI: 10.1143/JJAP.45.L690
KEYWORDS:SiC, defect, etching, chlorine, oxygen, EBIC
- H. Matsunami:
Jpn. J. Appl. Phys. 43 (2004) 6835[JSAP].
- T. Kimoto, N. Miyamoto and H. Matsunami:
IEEE Trans. Electron Devices 46 (1999) 471[CrossRef].
- M. K. Das, J. J. Sumakeris, B. A. Hull, J. Richmond, S. Krishnaswami and A. R. Powell: Mater. Sci. Forum 483–485 (2005) 965.
- D. Nakamura, I. Gunjishima, S. Yamaguchi, T. Ito, A. Okamoto, H. Kondo, S. Onda and K. Takatori:
Nature 430 (2004) 1009[CrossRef].
- J. Takahashi, M. Kanaya and Y. Fujuwara:
J. Cryst. Growth 135 (1994) 61[CrossRef].
- M. Katsuno, N. Ohtani, J. Takahashi, H. Yashiro and M. Kanaya:
Jpn. J. Appl. Phys. 38 (1999) 4661[JSAP].
- M. Syvajarvi, R. Yakimova and E. Janzen: J. Electrochem. Soc. 147 (2000) 3519.
- Z. Y. Xie, C. H. Wei, L. Y. Li, Q. M. Yu and J. H. Edgar:
J. Cryst. Growth 217 (2000) 115[CrossRef].
- H. Nakagawa, S. Tanaka and I. Suemune:
Phys. Rev. Lett. 91 (2003) 226107[APS].
- H. Habuka, S. Oda, Y. Fukai, K. Fukae, T. Takeuchi and M. Aihara:
Jpn. J. Appl. Phys. 44 (2005) 1376[JSAP].
- M. Ikeda: Dr. Thesis, Department of Electronics, Kyoto University, Kyoto, 1980.
- T. Hatayama, H. Yano, Y. Uraoka and T. Fuyuki: Microelectron. Eng. 83 (2006) 30.
- S. Nitani, T. Hatayama, K. Yamaguchi, H. Yano, Y. Uraoka and T. Fuyuki:
Jpn. J. Appl. Phys. 44 (2005) L1271[JSAP].
- M. Kitamura, N. Usami, T. Sugawara, K. Kutsukake, K. Fujiwara, Y. Nose, T. Shishido and K. Nakajima:
J. Cryst. Growth 280 (2005) 419[CrossRef].